Effect Of pH On The Physicochemical Properties Of MoVTeNbOx Catalysts For Oxidation Of Propane To Acrylic Acid
Journal: International Journal of Scientific & Technology Research (Vol.5, No. 1)Publication Date: 2016-01-15
Authors : Syazwani M.N; Irmawati R; Taufiq-Yap Y.H; Zainuddin; N.;
Page : 40-45
Keywords : Index Terms microwave-assisted; MoVTeNbOx mixed metal oxide; pH; post treatment; propane oxidation;
Abstract
Abstract Mo1.0V0.3Te0.23Nb0.12 mixed metal oxide catalysts were prepared via slurry method followed by microwave irradiation. The pH 1 3 5 and 7 of the synthesis solution was shown to affect physicochemical properties of the catalysts. XRD analysis revealed that the monophasic orthorhombic M1 phase Te2M20O57 M Mo V and Nb was only developed when pH was 1. This catalyst displayed BET surface area 18.0 m2g the highest among other samples after post treatment and suggested the elimination of hexagonal M2 phase. The sample was also highly reducible with reduction temperature coincide very well with the temperature of catalytic reaction. Therefore this catalyst was also active and selective for anaerobic propane oxidation to acrylic acid.
Other Latest Articles
- Comparison Of Antibacterial Effects Between Aloe Vera And Sodium Fluoride On The Amount Of Streptococcus Mutans Colony ATCC In Vitro
- Count Data On Cancer Death In Ohio A Bayesian Analysis
- Physico-Chemical And Microbiological Quality Of Some Consumer Preferred Plain Set Yoghurts Sold In Matara Municipal Area Of Sri Lanka
- Microbial Profiling Of Cyanobacteria From VIT Lake
- Legal Protection Against The Dance Creator In Indonesia
Last modified: 2016-04-24 17:52:56