Investigation Antiwear Properties of Lubricants with the Geo-Modifiers of Friction
Journal: Tribology in Industry (Vol.39, No. 3)Publication Date: 2017-09-20
Authors : I. Levanov A. Doykin E. Zadorozhnaya R. Novikov;
Page : 302-306
Keywords : Lubricants; Gear oils; Geo-modifiers of friction; Antiwear properties;
Abstract
The article describes the influence of the geo-modifiers of friction on the antiwear properties of lubricants. Geo-modifiers of friction are the fine powders of mineral materials. This work is directed on the investigation the influence of the geo-modifiers of friction in the form of the hard lubricant compositions, which based on a mineral serpentine, on the anti-wear properties of greases and gear oils. This composition is the fine powder serpentine with the addition of components such as chalk, borax, kaolin and talc. We compared the antiwear properties of the greases without geo-modifiers of friction and the antiwear properties of greases containing the geo-modifiers of friction from 0.5 % to 3 %. The Litol-24 and transmission oil TAD-17 was used for testihg. The four-ball machine of friction was used for tests accordance with GOST 9490-75. As geo-modifiers the serpentine was used, the fraction of which has a size from 0.87 microns to 2.2 microns. Such parameter as the wear scar diameter was used for evaluation of the antiwear properties of lubricants. As a result of tests it was established that the antiwear greases properties improved on 26-50 % depending on the concentration of the geo-modifiers of friction based on the pure serpentine.
Other Latest Articles
- OPTIMALISASI PEMENUHAN HAK KORBAN KEKERASAN TERHADAP PEREMPUAN MELALUI PUSAT PELAYANAN TERPADU
- KEBEBASAN BEREKSPRESI DALAM PERSPEKTIF HAK ASASI MANUSIA: PERLINDUNGAN, PERMASALAHAN DAN IMPLEMENTASINYA DI PROVINSI JAWA BARAT
- Effect of Nanoadditives on the Wear Behavior of Spheroidal Graphite Cast Irons
- Adding Aramid Fibers to Improve Tribological Characteristics of two Polymers
- Effect of Graphene Nanoplatelets (GNPs) on Tribological and Mechanical Behaviors of Polyamide 6 (PA6)
Last modified: 2017-10-06 16:49:09