Analysis on Quenching Cracks of Engine Crankshaft
Journal: International Journal of Engineering Research (IJER) (Vol.6, No. 11)Publication Date: 2017-11-01
Authors : Jinglong Fan Fulong Chen;
Page : 475-478
Keywords : crack; hardening; martensite; austenite;
Abstract
Engine crankshaft of cracks macro and micro were analyzed by morphological characteristics and quench cracks organization identified as the quenching crack, but further study showed that the root cause of this quenching cracks generated not due to the heat treatment process or other causes, but due to poor uniformity of the hot iron casting, elements gathered along the grain boundary segregation
Other Latest Articles
- 3D modeling of Complex Structure based on AutoCAD VBA
- Design of Quick-sensing Device for Temperature Difference Generation Environment Based on Single Chip Microcomputer
- Analysis on the Generation and Control of Strip Defects on the Surface of Color Coated Plates
- Computational Economics
- Fluoride Removal Efficiency of Commercially Available Reverse Osmosis Water Purifying Systems in Removing Fluoride Ions from Drinking Water in India
Last modified: 2017-11-12 02:52:13