Macroscopic quality evaluation of lacquered steel sheets

His paper deal with the evaluation of quality of lacquered sheets with different pre - treatments after corrosive loading. Samples will be divided into groups according to the type and duration corrosion loadings. After exposure to corrosive salt mist corr osion chambe r, the samples will be evaluated macroscopically according to relevant standards. Low degradation after all time corrosion load was on the sample pre - treated with an alkaline degreasing in combination with a yellow chromating and the samples pre - treated wi th an alkaline d e- greasing in combination with surface passivation. On these samples showed no loss of adhesion to the base material and the ev aluation of delamination due to corrosion during loading had a low degree of degradation. Surfaces after the cross - cut test did not for both sets of sa m- ples after corrosion load all times no defects in the adhesion layer