Characterization of Pr6O11-Ag2O-B2O3 Glasses.
Journal: International Journal of Engineering Sciences & Research Technology (IJESRT) (Vol.3, No. 5)Publication Date: 2014-05-30
Authors : Jagadeesha Gowda.G.V; B.Eraiah;
Page : 228-232
Keywords : Silver borate glass; Praseodymium; XRD; DTA and MAS-NMR.;
Abstract
Silver borate glasses doped with Praseodymium of different concentration has been prepared by melt quench technique. X-ray diffraction pattern shows that there is no sharp peak it confirms the amorphous nature of the present glasses. The glass transition temperature (Tg) of this glass system have been studied using the Matac MBS-8000 Digital Signal Processing and Conventional Thermal Analysis (DTA) method. The Tg of these glasses increases with increase in concentration of Pr6O11 except at 0.2 mol%Tg value is lower. We investigate the network structure of Pr6O11-Ag2O-B2O3 glass by 11B magic angle spinning (MAS)-nuclear magnetic resonance (NMR) which shows the presence of sharp peak at around 18 ppm. Formation of B4 units is assumed to be occurring initially through the formation of oxygen bridges between [BO3/2] 0 units in B2O3.
Other Latest Articles
- A Survey of Benchmarking Techniques for Network Performance.
- Analysis of Diverse Reversible Watermarking Methods in Image Processing.
- Advanced AODV Routing Algorithm with Energy Efficiency in MANET.
- Neural Network Modeling and Sorption of As III with Zinc Oxide Nanoparticle Bounded on Activated Silica using Ocimum Sanctum.
- Heat and Mass Transfer on MHD Boundary Layer Flow of a Chemically Reacting non-Newtonian fluid over a Stretching Sheet with Suction.
Last modified: 2014-06-04 18:46:37