Microstructure and Mechanical Properties of Hot Pressed 16.5CR Ferritic ODS Steel Developed Through Mechanical Alloying
Journal: International Journal of Mechanical and Production Engineering Research and Development (IJMPERD ) (Vol.8, No. 2)Publication Date: 2018-04-30
Authors : G. Dharmalingam R. Mariappan; M. Arun Prasad;
Page : 699-708
Keywords : Ferritic ODS Steel; Mechanical Alloying (MA); Vacuum Hot Pressing (VHP); Crystallite Size.& Hot Pressing;
Abstract
Two different ferritic oxide-dispersion-strengthened (ODS) steels compositions Fe–16.5Cr–0.89Mn-0.3Y O - 2 3 2ZrO (Sample1) and Fe–16.5Cr–0.89Mn-0.3Y O -2ZrO -2Al (Sample2) were prepared through Mechanical Alloying 2 2 3 2 (MA) and X-Ray Diffraction (XRD) pattern were taken at different time intervals for confirming the Nano-crystallite size. O Milled powders were consolidated at 1170 C at three different pressure levels of 30, 40 and 60 MPa respectively. Densification studies, microstructural examination ,and mechanical properties evaluation were analyzed and reported in the current study. MA of the hot pressed powder at 60 MPa obtained the highest density, hardness ,and tensile strength compared with another pressure compact irrespective of its composition. Aluminum addition in the ferritic ODS steel lowers the density, hardness ,and elongation of the ferritic ODS steel samples.
Other Latest Articles
- Assessment of Combustion, Performance and emission Features of Biodiesel in a Thermal Barrier Coated Diesel Engine
- CFD Analysis on Buble Growth and Bubble Departure in Pool Boiling
- Buckling Analysis of Carbon Epoxy Trailing Edge Wing Rib
- Design and Analysis of Micro Air Vehichle with Zimmerman Planform
- Experimental Investigation on Hardness, Microstructure and Surface Roughness of Maraging Steel Parts Produced by Direct Metal Laser Sintering Technique
Last modified: 2018-07-23 20:46:40