PROPERTIES OF TAWN AND TAN/TAWN COATING FILM DEPOSITED ON WC-CO-BASED CEMENTED CARBIDE USING MAGNETRON SPUTTER ION PLATING
Journal: PEOPLE: International Journal of Social Sciences (Vol.4, No. 2)Publication Date: 2018-07-14
Authors : Tadahiro Wada;
Page : 256-265
Keywords : Coating Technology; Physical Vapor Deposition Coated Tool; TaWN Coated Tool; Hardened Steel;
Abstract
Titanium based coating films are generally used as the coating film. In this study, the thickness, hardness and scratch strength of TaWN and TaN/TaWN coated tools were measured. The substrate used was a cemented carbide ISO K10. The work piece used was a hardened steel AISI D2. This work piece was turned with the TaWN and the TaN/TaWN coated tools. The tool wear of the TaWN and TaN/TaWN coated tools was investigated. Furthermore, the TaN coated tool was also used. (1) Droplets on the surface of both the TaWN and TaN/TaWN coating films were negligible. (2) The hardness of the TaWN and TaN/TaWN was 2340 HV0.25N and 2630 HV0.25N, respectively. (3) The critical load of both the TaWN and TaN/TaWN coated tools was over 130 N. (4) The friction coefficient of the TaN/TaWN and TaN was 0.44 and 0.53, respectively. (5) The wear rate of the TaN/TaWN coated tool was slower than that of the TaN or TaWN coated tool.
Other Latest Articles
- The Contested and Expanding Meaning of Democracy
- The Concept of Gender Crossing in the Deirdre McCloskey’s Theory
- Effectiveness and Outcome Moderators of Computer-Based Health Education for an Adult Population: A systematic Review of MetaAnalytic Studies
- The Influence of Time Perspective on Retention in United States Army Personnel
- Differences in Black Student Enrollment in Texas Doctoral Programs Over Time
Last modified: 2018-11-02 18:19:41