STUDY ON MORPHOLOGY AND MECHANICAL PROPERTIES OF STOICHIOMETRICALLY DEVELOPED AL-CU-MG CAST ALLOY
Journal: International Journal of Mechanical Engineering and Technology(IJMET) (Vol.10, No. 3)Publication Date: 2019-05-22
Authors : RAKESH KUMAR; VARINDER SAHNI;
Page : 1556-1565
Keywords : 6xxx Al alloys; Mechanical properties; Solution treatment Temperature; Thermal Aged temperature;
Abstract
The present study was carried out to investigate the mechanical properties of newly developed cast aluminum alloy with the (1.0 at. %) of copper and (1.0 at. %) magnesium addition in the mole ratio of 1:1:1 of Al-Cu-Mg in as - cast and thermally aged conditions. The atomic weight (at. %) selection of Cu-Mg on the basis of stoichiometric calculations, 1 unit (at. %) of copper and 1 unit (at. %) of magnesium preheated at 200C were mixed in liquid aluminium base material, heated in an electric furnace and melting temperature was kept at 750C for about 10 min alone and this melt was hold at 7300C with alloying additions of copper and magnesium for about 30 min to ensure complete homogenisation, Further, this liquidous aluminium metal matrix was stirred at 800 rpm for five minutes and poured at temperature 7000C 10 0C in permanent mild steel mould preheated at 2000C in order to achieve as- cast aluminium alloy.
Other Latest Articles
- FUNDAMENTALS OF SPECIFICATION FOR SORBENT IN DEFLUORIDATION OF DRINKING WATER
- COST ANALYSIS OF ENDOSCOPIC PROCEDURES IN A TERTIARY CARE HOSPITAL IN SOUTH INDIA
- INFORMATION TECHNOLOGY ARCHITECTURE DESIGN TO AUTOMATE ENTERPRISE BUSINESS PROCESS USING TOGAF ADM
- OPTIMIZATION OF DRESSING PARAMETERS FOR GRINDING TABLET SHAPE PUNCHES BY CBN WHEEL ON CNC MILLING MACHINE
- INFORMATION TECHNOLOGY ARCHITECTURE DESIGN TO AUTOMATE ENTERPRISE BUSINESS PROCESS USING TOGAF ADM
Last modified: 2019-05-23 23:15:47