COMPARISON STUDY BEWTWEEN THE RECOVERY BEHAVIOR OF DEFORMED QUENCHED, PRE-ANNEALED AND PULSED LASER DAMAGED Fe50Ni50 ALLOY BY MAGNETIC MEASUREMENTS
Journal: INTERNATIONAL JOURNAL OF ENGINEERING TECHNOLOGIES AND MANAGEMENT RESEARCH (Vol.6, No. 5)Publication Date: 2019-05-30
Authors : A.R. Ali E. Takla K.K. Meleka;
Page : 127-134
Keywords : Fe50Ni50; Ferromagnetic Alloy; Magnetic Properties; Plastic Deformation; Activation Energy; Order of Reaction.;
Abstract
Through the magnetic measurements, isochronal annealing experiments in the temperature 25- 950 ºC of deformed, quenched, pre-annealed and pulsed laser damage samples Fe50Ni50 alloy revealed the existence of three annealing stages I, II and III in the annealing spectrum of heavily cold-worked by observing the associated changes in maximum magnetic permeability (µmax) on the magnetic field(H) for different annealing temperature. The first annealing stage I appeared in the temperature range from125-500 ºC and it was activated by energy 1.05 eV. It was attributed to the short range order caused by the long range migration of vacancies. The second annealing stage II appeared in the temperature range from 550-750 ºC and it was activated by 1.82 eV, it is associated with an increase in µmax due to the dissociation of vacancy clusters formed during stage I. The third annealing stage III appeared in the temperature range from 750-825 ºC and it was activated by 3.04 eV, it was related to the climb motion of dislocation during the recrystallization process.
Other Latest Articles
- A CASE REPORT OF MAYER ROKITANSKY KUSTER HAUSER SYNDROME
- A RARE CASE OF CHOREA GRAVIDARUM
- FUNDAL RUPTURE OF UTERUS FROM PREVIOUS ABORTION-RARE CASE REPORT
- The Economic Burden of Bleeds and Transfusions in Selected Surgeries: A Retrospective Multi Center Analysis from the US Perspective| Biomed Grid
- Collateral Discoveries Done During Research About Time & Space| Biomed Grid
Last modified: 2019-05-31 14:26:24