Tribological properties of PPS/PA46 polymer blends
Journal: Research on Engineering Structures and Materials (Vol.6, No. 3)Publication Date: 2020-09-15
Authors : Ferhat Yıldırım Mustafa Aydın Hakan Yetgin;
Page : 271-282
Keywords : Fiber Glass Reinforcement; Hybrid Composite; Polyamide 46; Polyphenylene Sulfide; Wear;
Abstract
In this study, the tribological performance of originally 40 wt.% fiber glass reinforced polyphenylene sulfide (PPS-G), polyamide 46 (PA46) and their blends were studied at dry sliding conditions. The materials were mixed and extruded on the twin screw extruder. The blends were dried and tribological test specimens were manufactured by using the injection machine. Wear tests were performed with the configuration of a polymer pin on a rotating X40CrMoV5-1 steel disc. Test conditions were atmospheric conditions having 60, 90, 120 N loads and 0.5, 1.0, 1.5 m/s sliding speeds. The obtained results proved that the coefficient of friction for PPS-G, PA46 and their blends is decrease while the applied load and sliding speed values are increase. On the other hand, the specific wear rate is in increase while the applied load and sliding speed values are in increase.
Other Latest Articles
- Tuning the properties of silica aerogels through pH controlled sol-gel processes
- An investigation of high temperature effect on pumice aggregate light mortars with brick flour
- Evaluation of different cases of soft story formation for mid-rise RC buildings
- Nonlinear vibrations of a cantilevered pipe conveying pulsating two phase flow
- Impact of energy efficient design parameters on energy consumption in hot-humid climate zones
Last modified: 2020-09-25 21:35:41