Study Dielectrically Behavior of the (Ba TiO3) and (Ba TiO3/Ni0.7 Zn0.3 FeO4) Nano Composites

In this research, nano composites were manufactured from (Ba TiO3andNi0.7 Zn0.3 FeO4) nano compound s. (Ni0.7 Zn0.3 FeO4) Nano compound was added to Ba TiO3 by 20 % and 50 %. These materials were mixed in a solid reaction and formed under pressure 5.4. MPa were treated at 1100 C. It has been observed that the dielectric properties of Ba TiO3 decreased with the addition of Ni0.7 Zn0.3 FeO4) Nano compound in general, this is due to the generation of pores in the composite.