Effects of Shot Peening Pressure on Friction and Wear of High Pressure Cold Sprayed Ti-6Al-4V Coatings Under Dry and Lubrication Conditions
Journal: Tribology in Industry (Vol.45, No. 3)Publication Date: 2023-09-15
Authors : Nay Win Khun Pham Quang Trung Adrian Wei YeeTan Wen Sun Erjia Liu David Lee Butler;
Page : 472-486
Keywords : Cold spray; Shot peening; Ti64 coating; Microstructure; Hardness; Wear;
Abstract
The effects of shot peening pressure (SPP) (10-60psi) on the wear resistance of high-pressure-cold-sprayed Ti-6Al-4V coatings (HPCSTi64-Coats) were investigated against 100Cr6 steel with or without mineral oil lubricant (MOL), which have not been reported yet. The specific wear rate (SWR) of the HPCSTi64-Coat with the SPP of 60psi was 29% lower than that of the one without shot peening (SP). With the MOL, the SWR of the HPCSTi64-Coat without SP was 40.8% higher than that of the one with 10psi. The SWR of the HPCSTi64-Coat became higher with higher SPP while the SWR of the HPCSTi64-Coat with 60psi was 76.5% higher than that of the one with 10psi. Therefore, the best SPP for the best bearing surface of the HPCSTi64-Coat with the MOL was 10psi. In spite of that, the HPCSTi64-Coats lubricated with the MOL had smaller SWRs for all the SPPs so that the SWRs of the HPCSTi64-Coats with the SPPs of 0 and 60psi were 2.4 and 0.9 times higher, respectively, in the tribo-tests without than with the MOL.
Other Latest Articles
- Current Directions and Trends of Cancer Chemotherapy: An Overview of the Recently Approved Small-Molecules Anticancer Drugs in the Past Decade |Biomedgrid
- Multidisciplinary Integrated Care in Atrial Fibrillation (Micaf): ASystematic Review and Meta-Analysis |Biomedgrid
- Use of Environmental Enrichment as a Clinical Methodology During Acute Experimental Infection by Trypanosoma Cruzi |Biomedgrid
- Inclusion of Underrepresented Entrepreneurialminded Postdocs in High-tech Startups Increases U.S. Competitiveness |Biomedgrid
- Vaccinations, The Journey So Far and The Road Ahead |Biomedgrid
Last modified: 2023-09-28 15:59:03