The Tensile Strenght Properties Effect Of Rice-Husk Ash As On The Composite Of Plastic Drinking Bottle Waste
Journal: International Journal of Scientific & Technology Research (Vol.4, No. 4)Publication Date: 2015-04-15
Authors : Maulida; Syahri Dani; Faisal Bukhory;
Page : 66-69
Keywords : Index Terms composite; extruder; tensile strength; rice husk ash; plastic drinking bottle waste.;
Abstract
Abstract Rice-husk ash has a potential to be filler in composite. The study on rice-husk ash utilitation as afiller in polyethylene terephthalate PET matrix of plastic drinking bottle waste was conducted in order to find the ratio of rice-husk ask and PET matrix that would result the best tensile strength which was characterized by using scenning electron microscopy SEM. In this study the PET of plastic drinking bottle waste firstly was cut into smaller pieces and was extruded with the temperature of 265 o C. Then it was mixed with rice-husk ash on ratio of PET plastic drinking bottle waste and rice-husk ash of 955 9010 and 8515. After that it was extruded at temperature of 265 o C before it was pressed by hot press at temperature of 265 o C for five minutes. The highest tensile strength was achieved at 3462 MPa with elongation at break a round 14375 and youngs modulus of 34882 MPa for the ratio of 8515.
Other Latest Articles
- Video Malware - Behavioral Analysis
- Big Data Clustering Using Genetic Algorithm On Hadoop Mapreduce
- Al-7075 Malzemesinin Freze Tezgh26305nda Delme 2630426351leminde Farkl26305 Devir Ve 26304lerleme H26305zlar26305 26304in Olu26351an Titre26351imlerin 26304ncelenmesi
- Experimental Study For Pizometric Head Distribution Under Hydraulic Structures
- Optimization Of Bleaching Parameters By Whiteness Index And Bursting Strength Of Knitted Cotton Fabric
Last modified: 2015-06-28 04:09:59