Pembuatan bahan penyamak nano nabati dan aplikasinya dalam penyamakan kulit
Journal: Majalah kulit, karet, dan plastik (Vol.31, No. 1)Publication Date: 2015-06-30
Authors : Herminiwati Herminiwati; Sri Waskito; Christiana Maria Herry Purwanti; Prayitno Prayitno; Dwi Ningsih;
Page : 15-22
Keywords : vegetable tanning material; nano particle; acacia bark; extraction; planetary ball mill;
Abstract
This study aimed to create nano vegetable tanning materials of acacia bark extract. The process started with size reduction of acacia bark (16.7 mm x 4.9 mm x 1.8 mm), followed by counter current extraction of acacia bark with water at 80ºC with 1:3 bark to water ratio in order to obtain extracts with density of 9-10ºBe. Drying was done with a spray dryer. Particle size of the resulting powders was measured with particle size analyzer. Planetary ball mill was used for 6 hours to obtain average particle size of 72.9 nm. A variety of vegetable tanning materials were applied in the vegetable tanning process with varied concentrations of 15, 20, and 25%. The use of 25% nano vegetable tanning material of acacia bark extract gave the best results compared to liquid extract of acacia bark and mimosa. The properties of the leather obtained were tensile strength of 27.04 kg/cm2, elongation at break of 50%, shrinkage temperature of 84oC, and degree of tannage of 79.65%.
Other Latest Articles
- Karakteristik plastik biodegradabel dari limbah plastik polipropilena dan pati biji durian
- Pemanfaatan limbah kulit singkong termodifikasi alkanolamida sebagai bahan pengisi dalam produk lateks karet alam: Pengaruh waktu vulkanisasi
- Pengaruh rasio MBTS/ZDEC pada campuran karet alam dan etilen propilen diena yang dibuat dengan teknik kontrol migrasi curatives
- Pemanfaatan limbah padat industri karet remah (crumb rubber) untuk pembuatan kompos
- Optimasi waktu reaksi pembentukan kompleks indofenol biru stabil pada uji n-amonia air limbah industri penyamakan kulit dengan metode fenat
Last modified: 2016-02-09 11:39:35