Pengaruh penggunaan nitril butadiene rubber dan pale crepe pada pembuatan sol karet untuk sepatu pengaman

Rubber sole for safety shoes was different on physical specification with general sole, especially on abrasion resistance and oil resistance. The objective of the study was to determine the effect of nitril butadiene rubber and pale crepe on physical properties of vulcanized rubber sole for safety shoes. Rubber sole for safety shoes was produced by blending pale crepe and nitril butadiene rubber with ratio of : 50/50; 60/40; 70/30 and 80/20 phr, respectively. Carbon black as filler was also variated with, 40 ; 50 and 60 phr. Compounding processing used two roll mill machine and vulcanized rubber sole was by using pressed use hydraulic press machine. The results showed that vulcanized rubber sole for safety shoes with good quality consist of pale crepe and NBR 80/20 phr and carbon black 40 phr, which was characterized by tensile strength 16.81 N/mm2, tear strength 11.68 N/mm, density 1.12 g/cm3, abrasion resistance 58.51 mm3, hardness 71.60 shore A, resistance to cut growth 30.000 times was 1.15 mm and oil resistance 65.44%, respectively. The quality parameters was complied with standard quality of SNI 0111 : 2009, for safety shoes from leather and vulcanized rubber sole that fulfill oil reistance parameter.