Pemanfaatan ter sebagai softener dalam pembuatan karet riklim
Journal: Majalah kulit, karet, dan plastik (Vol.22, No. 1)Publication Date: 2006-12-30
Authors : Arum Yuniari;
Page : 26-31
Keywords : reclaimed rubber; scrap rubber; coal tar; softener;
Abstract
The aims of this research was to study the effect of Coal Tar as softener for reclaim rubber production from waste of rubber of tyre rethreading as input materials was scrap rubber. Coal Tar as softener was used with variation; 2,5; 5; 7,5; 10; 12,5 and 15% respectively from total scrap rubber. Reclaimed rubber was made at temperature 1200C for 1 hour in autoclave and than it was subsequently ground with two rolls mills. The characteristics of the reclaimed rubber was tested for the vulcanization and physical properties. The results showed that Coal Tar could be utilized as softener for reclaimed rubber. Reclaimed rubber production containing Coal Tar 15% would give good vulcanization and physical properties. The vulcanization 1062 seconds, maximum torque 39,08 kgf-cm, minimum torque 4,71 kgf-cm. Good physical properties : tensile strength 80,74 kg/cm2 elongation at break 444,62%, hardness 49 shore A, tear strength 40,39 kg/cm, density 1,15 g/cm3, abrasion resistance 1,87 mm3/kgm, and no crack detected on the flex cracking test of 150 kcs.
Other Latest Articles
- Penggunaan zat warna alam untuk kulit non konvensional
- Penggunaan zeolit alam untuk mengurangi kandungan krom dan nh4+ dalam air limbah penyamakan kulit
- Rekayasa alat daur ulang limbah padat industri penyamakan kulit untuk pembuatan insol dan kertas karton
- Pemanfaatan minyak kulit biji jambu mete sebagai substitusi karet stirena butadiena pada kompon karkas ban kendaraan bermotor
Last modified: 2016-02-09 17:55:57