Karakteristik karet ebonit yang dibuat dengan berbagai variasi rasio RSS I/Riklim dan jumlah belerang
Journal: Majalah kulit, karet, dan plastik (Vol.20, No. 1)Publication Date: 2004-12-30
Authors : Penny Setyowati; Sutarti Rahayu; Supriyanto Supriyanto;
Page : 10-14
Keywords : Ebonite; reclaim; sulphur; natural rubber;
Abstract
The aim of the research was to study the influence of utilization of sulphur and reclaim rubber on the characteristics of ebonite rubber, and also to determine the optimum utilization of reclaim rubber and sulphur which yield good physical properties. Ebonite rubber was made by special natural rubber of RSS I (Ribbed Smoke Sheet I) mixed with reclaimed rubber at ratio 80/20, 70/30 and 60/40 part hundred rubber/part hundred rubber (phr/phr) and utilization of sulphur 30, 40, and 50 phr and also additives respectively. Mixing was done by using open mill, and vulcanization was conducted at early temperature 1200C for 2 hours, and it was continued by post curing at temperature 1500C for 2 hours. The physical properties such as tensile strength, elongation at break, D shore hardness, and izod impact of ebonite rubber vulcanized were determined. The result indicated that characteristics of ebonite rubber was significantly influenced by the amount of added sulphur and 40 phr reclaim rubber or at ratio of RSS I to reclaim rubber 60 to 40 phr/phr. However, the physical properties of ebonite rubber was able to meet the standard quality of group 2 regarding to Classification Hard Rubber issued by ASTM D 2135.
Other Latest Articles
- Rancang bangun industri penyamakan kulit ikan pari
- Kulit ikan kakap tersamak: Exotic dan prospektif
- Pengaruh rss/sbr dan filler CaCO3 terhadap sifat fisis kompon karpet karet
- Pengaruh penerapan teknologi vakum dan non-vakum terhadap umur simpan pangan berminyak
- Pemanfaatan arang aktif sekam padi untuk bahan pengisi keset karet
Last modified: 2016-02-10 10:25:53