Pengaruh carbon black pada pembuatan plastik untuk irigasi sistem tetes
Journal: Majalah kulit, karet, dan plastik (Vol.17, No. 1)Publication Date: 2001-12-30
Authors : Arum Yuniari; Dwi Wahini Nurhajati; Niken Karsiati;
Page : 26-32
Keywords : ;
Abstract
The objective of this experiment was to know the influence carbon black was added to the plastics for drip irrigation systems. Plastics of 0,2 mm thickness for drip irrigation system was made from mixing of lwo density polyethylene (LDPE), high density polyethylene (HDPE) and carbon black by a blown film machine on the fixed processing condition. The investigated carbon black content were 0; 2,5; 5; 7,5; and 10 phr respectively and LDPE/HDPE ratio were 0/100, 50/50, 100/0 respectively. The physical properties tes showe and increasing of carbon black decreasing tensile strength, elongation at break, tear strength and brittleness. The best formulation was consist of HDPE 100 phr and carbon black 10 phr, with the physical properties as follows : tensile strength 158 kg/cm2, elongation at break 140%, and tear strength 91,46 kg/cm2.
Other Latest Articles
- Pembuatan kulit untuk label
- Penggunaan ekstrak kayu nangka (artocarpus heterophyllus) sebagai bahan pewarna untuk kulit
- Resin poliurethan sebagai bahan pelapisan aksesoris logam untuk mengurangi cacat produk barang kulit
- Zeolit sebagai bahan pengisi pada kompon karet ditinjau dari sifat fisika vulkanisatnya
- Penggunaan lemak fleshing industri penyamakan kulit untuk pembuatan sabun mandi
Last modified: 2016-02-10 12:42:02