COMPARATIVE INHIBITIVE EFFECT OF HYDROXYETHYLCELLULOSE ON MILD STEEL AND ALUMINIUM CORROSION IN 0.5M HCL SOLUTION
Journal: Academic Research International (Vol.1, No. 3)Publication Date: 2011-11-15
Authors : Innocent O. Arukalam Ifeanyi K. Nleme Ambrose E. Anyanwu;
Page : 492-498
Keywords : Aluminium; Hydroxyethylcellulose; corrosion inhibition; corrosion current; Inhibition Efficiency;
Abstract
The inhibitive effect of HEC on Mild steel and Aluminium corrosion in 0.5M HCl solution under atmospheric exposure was studied using weight loss method. From the results obtained, it was observed that the corrosion rate was higher in Aluminium than in Mild steel. Inhibition efficiency and surface coverage were however, found to be higher in Mild steel than in Aluminium. In addition, corrosion current was determined. From our results, the corrosion current was higher in Mild steel than in Aluminium.
Other Latest Articles
- THE INHIBITION OF ALUMINIUM CORROSION IN HYDROCHLORIC ACID SOLUTION BY HYDROXYETHYLCELLULOSE
- THE DILEMA OF OZONE LAYER DEPLETION, GLOBAL WARMING AND CLIMATE CHANGE IN TROPICAL COUNTRIES: A REVIEW
- CLIMATE CHANGE, GLOBAL WARMING AND ADAPTABILITY FOR SUSTAINABLE GROWTH AND DEVELOPMENT IN NIGERIA
- INTERNET AS A COST EFFECTIVE TELEPHONE NETWORK OF THE WORLD
- EFFECT OF BASIL (OCIMUM BASILICUM L.)ON COCCIDIAL INFECTION IN BROILER CHICKS
Last modified: 2013-08-30 11:56:57