LIGHTWEIGHT CONCRETE BASED GRANSHLAK

Journal: Bulletin of Prydniprovs'ka State Academy of Civil Engineering and Architecture (Vol.2016, No. 2)

Publication Date:

Authors : ; ;

Page : 62-74

Keywords : lightweight concrete secondary products industry; strength; density; wall material; cement;

Source : Downloadexternal Find it from : Google Scholarexternal

Abstract

Concrete advisable to obtain a low strength with local secondary resources for recycling and reduce the environmental burden on the environment. But it is important to design such concrete compositions with a reduced flow of cement. It is known that the coefficient of efficiency of use of cement in the concrete of the heavy and B10 is less than about 0.5, which is almost two times smaller than in class B15 concrete and above. Even lower coefficient of efficiency in light concrete cement low strength. Therefore, it is important to find patterns determining the composition of lightweight concrete based on local-products industry with more efficient use of cement in them. Purpose.. Based on the analysis of earlier research results, including with the use of methods of mathematical planning of experiments to determine the concrete contents, which can provide the requirements for the underlying layers of the floor, the compressive strength of which should correspond to the class B5. It is important to provide the required strength at minimum flow of the cement, which is the most expensive and energy-intensive part of concrete. Conclusion. Analysis of the test results of control samples of concrete in 28-day-old, the following laws. The required tensile strength of concrete compressive strength of 7.0 MPa can be obtained in the test range when used in formulations as a filler as the Dnieper hydroelectric power station fly ash and tailings Krivoy Rog iron ore YuGOK. To ensure providing the required characteristic strength of the concrete in the underlying layers of the floor is advisable to use a nominal composition per cubic meter of concrete: cement 160 kg granshlaka Plant named after Petrovsky, 675 kg of fly ash Dnieper HPP 390 kg, 400 kg of sand, 230 liters of water. Thus, while ensuring rational grain composition components can obtain the desired strength lightweight concrete based granshlaka plant Petrovsky, using as fillers tailings Krivoy Rog iron ore YuGOK or fly ash Dnieper TPP. In order to ensure the required strength lightweight concrete class B5 based on local-products industry enough cement to 150 kg per cubic meter of concrete.

Last modified: 2016-04-05 20:12:44