The effect of using hybrid nanomaterials on drying shrinkage and strength of cement pastes
Journal: Nanotechnologies in Construction: A Scientific Internet-Journal (Vol.8, No. 2)Publication Date: 2016-04-12
Authors : Saaid I. Zaki; Hossam A. Hodhod; Mostafa A. Mahdi;
Page : 109-134
Keywords : nanosilica; nanoclay; hybrid nanomaterials;
Abstract
The aim of this work is to study the effect of nanomaterials on the properties of cement paste, the experimental program included three parts: a- two types of nanosilica, locally produced NS1 and imported NS2, b- nanoclay (NC) and c- Hybrid nanoparticles (NS1 & NC). In each part,
cement paste was used with different percentages of nanoparticles. Compressive strength and drying shrinkage tests were applied in each part on the cured and uncured samples. The results showed that the compressive strength improved in the cement paste mixtures in the cured condition, the optimum percentages was 1% for NS1, 1% for NS2, 5% for NC, and 5% (0.5%NS1 & 4.5%NC) for hybrid nanoparticles. The drying shrinkage increases with adding nanosilica and hybrid nanoparticles, while it decreases when adding NC.
Other Latest Articles
- Theses in the area of nanotechnologies and nanomaterials: novelties and practical application. Part 2
- New technical solutions in nanotechnology. Part 1
- Nanocomposite organomineral hybrid materials. Part 2
- Theses in the area of nanotechnologies and nanomaterials: novelties and practical application. Part 1
- Alternative technology of nanoparticles consolidation in the bulk material
Last modified: 2016-04-16 04:48:56