Minimizing Fabrication Time Of Calcium Modified Pbti03 Nanoceramics By HEBM Technique
Journal: International Journal of Scientific & Technology Research (Vol.5, No. 2)Publication Date: 2016-02-15
Authors : Sona Kumari; S. K. Sinha; R. K. Choudhary;
Page : 183-186
Keywords : HEBM; lead oxide; LCR meter; perovskite; stoichiometry; transition temp; XRD etc.;
Abstract
Lead titanate is one of the family member of ABO3 structure perovskite having piezoelectric as well as pyroelectric properties in nature. It shows highl ferroelectric property as ceramic materials. Ca modified lead titanate termed as P1-xCXT synthesized by HEBM at 270 C of room temperature. The stoichiometric ratio was taken as Pb1-xCaxTi03 where Ca0 was taken in various ratio . Structural and electrical properties were studied by taking measurement with standard instruments LCR metre. Analysis of XRD gives that doping of calcium produce a decrease in tetragonal size and hence the volume . As a result on A-site substitution observed. Graph of electrical parameters shows that impedence decreases exponentially with frequency.
Other Latest Articles
- Interaction With PC Tablets And Possible Emotional Responses
- Value-Added Business Based On Small Scale Of Fisheries A Case Study On Nortern And Shouthern Coasts Of Java Lamongan And Pelabuhanratu Regency Indonesia
- Assessment Of The Physicochemical Characteristics Of Soils In Major Cocoa Producing Areas In The Dormaa West District Of Ghana
- Seed Germination Behaviors Of Some Aerobic Rice Cultivars Oryza Sativa L After Priming With Polyethylene Glycol-8000 Peg-8000
- Conjoint Analysis As Robust Measure Leadership Preferences Evidence From The Military Service
Last modified: 2016-04-24 17:53:56