DAMAGE ANALYSIS OF DEGRADED SLITTING KNIFE
Journal: International Journal of Engineering Sciences & Research Technology (IJESRT) (Vol.5, No. 9)Publication Date: 2016-09-30
Authors : Ki - Woo Nam; Cheol - Su Kim; Seok - Hwan Ahn;
Page : 153-159
Keywords : Slitting Knife; Damage Analysis; Wear Test; Vic kers Hardness; Weibull Analysis;
Abstract
This study analyzed the damage to a slitting knife after cutting steel sheet s . Damages to the structure were observed and wear tests were conducted. In addition, the degradation on the damaged and undamaged parts was compared with a Vickers hardness test. Weibull statistical analysis was carried out in order to evaluate the reliabi lity of the Vickers h ardness measured data. Spalling of the edge portion occurred by degradation during use over a long period. Rough parts in the specimens were caused by damage because the slitting knife was used for 1 year. The friction coefficient and wear loss at the damaged parts of the knife edge were slightly larger from shock due to repetitive cutting operation. The Vickers hardness followed a two - parameter Weibull probability distribution
Other Latest Articles
- STRUCTURAL AND TRANSPORT PROPERTIES OF TE DOPED LAMNO3
- INFLUENCE OF MODIFICATION OF THE ACTIVATED CARBON ON THE ADSORPTION OF ATRAZINE: EQUILIBRIUM STUDY AND KINETICS
- SEISMIC RESPONSE OF STEEL STRUCTURE WITH MEGA BRACING SYSTEM
- REVIEW OF CLUSTERING UNCERTAIN DATA
- ASSESSMENT OF APPLICABILITY OF THE CAPITAL STRUCTURE MODELS FOR THE COMPANIES OF THE OIL AND GAS INDUSTRY
Last modified: 2016-09-08 16:52:37