EXPERIMENTAL STUDY ON EFFECTS OF FIBERGLASS AND FIBER WASTE IN CONCRETE MIXES
Journal: International Journal of Engineering Sciences & Research Technology (IJESRT) (Vol.5, No. 10)Publication Date: 2016-10-30
Authors : Mashair.A.Mohamed; Mansour Ahmed Moh; Nuha Moawia Akasha; Ibrahim.Y.I.Elgady;
Page : 485-493
Keywords : Concrete; Fiberglass; Fiber waste; Compressive strength.;
Abstract
In this research concrete mixes were tested to investigate the effect of fiber waste and fiber glass and evaluate the efficiency on fresh and hardened concrete for trying to produce a concrete with high strength. an experimental study was carried out to test for c ompressive strength of concrete for six types of concrete mixes each mixture were casted in the form of cubes were studied for 7 and 28 days, one of those mentioned mixes is a (control mix). Finally the results are compared with the normal conventional co ncrete (control mix). The main aim of this investigation is first to prepare the strength of concrete of compressive strength 25N/mm 2 with locally available ingredient and then to study the effect of different proportion of fiber waste and fiber glass in t he mix and to find the optimum range of the effective proportion. The various proportions considered are 0.1%, 0.2%, 0.3%, o.4%, o.5% of fiber glass and fiber waste from mixture weight respectively. the research was shown that the effect of fiber and fiber waste on the fresh concrete that the workability decreases as the proportion of the fiber waste and fiber glass additives increases, and for the hardened concrete the specific compressive strength increases up to 0.3% of the fiber waste and fiber glass co ntent of mixture weight, and also show’s beyond these mention proportioned that the compressive strength decreases.
Other Latest Articles
- ALGORITHM OF PACKING ITEMS INTO PATH - GRAPH WITH CONSTRAINTS ON ADJACENT NODES
- Influence of temperature of test on the mechanical properties for rail wheel steel with new system of alloyage
- POLYMER STRUCTURES: STUDIES ON THERMAL AND MICROBIAL REACTIVITY OF COPOLYMERS AND TERPOLYMERS OF [AZO - N - 4 - BROMOPHENYL] SUBSTITUTED MALEIMIDE CHAIN WITH ACRYLATES VINYLS
- IMPACT OF PRE - ACCESS ION ASSISTANCE OF EU IN DAIRY SECTOR
- IMAGE ENHANCEMENT USING AUTOMATIC SEGMENTATION TECHNIQUES
Last modified: 2016-10-15 21:32:00