Wear Analysis on 410 Stainless Steel Material by Hardening ProcessJournal: International Journal of Advanced engineering, Management and Science (Vol.3, No. 5)
Publication Date: 2017-05-08
Authors : Ram Subbiah; M. Harini; M. Maneesha; Jahangeer; R. Rajavel;
Page : 616-618
Keywords : Hardening; stainless steel; wear; hardness.;
The wear conduct of 410 stainless steel has been examined under a dry sliding contact at consistent load. It was found that hardening procedure was successful in enhancing the wear conduct of stainless steel material, advancing the property of pliability. A low temperature hardening has been completed for three distinct examples at a hour, a hour and a half, 120 minutes. Untreated stainless steel was utilized as a kind of perspective material and experienced wear test for comparison with different hardening samples. The hardening samples uncover that hard layers that are shaped which enhances the surface hardness. Small scale hardness estimations uncovered a critical increment in hardness after treatment. The layers were portrayed by optical magnifying lens and checking electron magnifying lens investigation.
Other Latest Articles
Last modified: 2017-06-06 01:01:40