Resistance of Composite Board Made from Sago Frond, Metroxylon sagoRottb. Against Rotting Fungi and Subterranean Termite
Journal: Jurnal Penelitian Hasil Hutan (Vol.32, No. 4)Publication Date: 2014-12-30
Authors : DeniZulfiana; Sukma S. Kusumah;
Page : 253-262
Keywords : ;
Abstract
This study aimed to examine the resistance of composite boards made of sago frond using polyurethane (PU) and phenol formaldehyde (PF) adhesives against rotting fungi and termite. Dimension and targeted density of composite board were 30 cm x 30 cm x 1 cm and 0.5 g cm , respectively. Composite boards were prepared by cold press machine for composite boards using PU resin as a binder and hot press machine for boards using PF resin under the following conditions: 25 kg cm for 24 hours in cold pressing process and 10 minutes in hot pressing process with 140 C of temperature. Solid content of liquid adhesives was 50% with resin content as variations in this study i.e. 10%, 12% and 14%. The boards were tested against JIS K 1571 2004. The results show the composite boards treated with PU and PF adhesiveswerenotresistanttorottingfungiandtermites.
Other Latest Articles
- Physico-Chemical Properties of Cajeput Oil's from
- Decay Capability of Ten Fungus Strains to Five Wood Species from East Kalimantan
- SEBAGAI BAHAN BAKU PADA PEMBUATAN ARANG AKTIF Aleurites trisperma Utilization of Kemiri Sunan Shell Waste as Raw Material in Manufacturing of Activated Charcoal
- The Effects of Charcoal and Wood Vinegar to Growth Increase and Carbon Store
- Anatomical Properties and Fiber Quality of The Least Known Wood Species:Families of Capparidaceae, Caprifoliaceae, Chloranthaceae and Compositae
Last modified: 2018-05-08 10:43:16