Micro-Structural Evolution Analysis and Assessment of Tribological Behaviour 425 of Nickel Alloy Reinforced with Sio2 and Al2o3 Hybrid Metal Matrix Composites
Journal: International Journal of Mechanical and Production Engineering Research and Development (IJMPERD ) (Vol.10, No. 2)Publication Date: 2020-05-30
Authors : Vidyasagar Shetty Vijaya Kumar; G. Purushotham;
Page : 421-430
Keywords : Nickel Alloy; SiO2; Al2O3; & Stir Casting;
Abstract
Hybrid Metal Matrix Composites (HMMCs) enhances the main properties like wear resistance and good microstructure, as well as it saves weight. Reinforced hybrid metal matrix composites attract because it enhances wear resistance properties. Many researches are going on in material science field to strengthen the wear resistance properties of the materials and improve the quality of the material. The present research work carried out to fabricate the SiO2 and Al2O3 reinforced Nickel based alloy. Reinforcement is added in matrix with 9% in weight SiO2 (Constant) and range 3% to 12% in weight Al2O3 in steps of 3% in weight. Induction furnace is used to melt the composites; the composites are machined and tested after casting. Evaluation of microstructure, wear resistance of hybrid metal matrix (Monel M-35-1+SiO2+ Al2O3 ) is done and analyzed. From results, it is clear that the SiO2 and Al2O3 added with Nickel alloy shows good microstructure and reduced wear properties of composites.
Other Latest Articles
- Microstructure and Dry Sliding Wear Behaviour of Lm6 Alloy Solidified 413 Under the Influence of Low Frequency Mold Vibration
- Synthesis of Ceramic Composite Material by Powder Metallurgy and Optimize Process Parameters in Regression Method in Machining Micro Abrasive Air Jet Erosion Tester
- Combined Impact of Internal Heating and Variable Viscosity on the Onset of Benard-Marangoni Double Diffusive Convection in a Binary Fluid Layer
- Effect of Variable Adiabatic Length on a Heat Pipe Performance
- Pressure Vessel Reinforcement Pad Design by Finite Element Analysis
Last modified: 2020-05-30 23:36:17