Mechanical, Spectroscopic and Micro-structural Characterization of Banana Particulate Reinforced PVC Composite as Piping Material
Journal: Tribology in Industry (Vol.38, No. 2)Publication Date: 2016-06-20
Authors : B. Dan-asabe; A.S. Yaro; D.S. Yawas; S.Y. Aku; I.A. Samotu; U. Abubakar; D.O. Obada;
Page : 255-266
Keywords : Particulate composite; Mechanical characterization; Spectroscopic analysis; Piping material;
Abstract
A banana particulate reinforced polyvinyl chloride (PVC) composite was developed with considerabley low cost materials having an overall light-weight and good mechanical properties for potential application as piping material. The specimen composite material was produced with the banana (stem) particulate as reinforcement using compression molding. Results showed that density and elastic Modulus of the composite decreases and increases respectively with increasing weight fraction of the particulate reinforcement. The tensile strength increased to a maximum of 42 MPa and then decreased steadily. The composition with optimum mechanical property (42 MPa) was determined at 8, 62 and 30 % formulation of banana stem particulates (reinforcement), PVC (matrix) and Kankara clay (filler) respectively with corresponding percentage water absorption of 0.79 %, Young’s Modulus of 1.3 GPa, flexural strength of 92 MPa and density of 1.24 g/cm3. Fourier Transform Infrared (FTIR) analysis of the constituents showed identical bands within the range 4000?1000 cm-1 with renown research work. Scanning Electron Microscopy (SEM) result showed fairly uniform distribution of constituents’ phases. X-Ray Fluorescence (XRF) confirms the X-ray diffraction (XRD) result of the presence of minerals of kaolinite, quartz, rutile and illite in the kaolin clay. Comparison with conventional piping materials showed the composite offered a price savings per meter length of 84 % and 25 % when compared with carbon steel and PVC material.
Other Latest Articles
- Reduction and Maintance of Turbochargers by Applying Valid Tribological Constructing
- Investigations into the Degradation of PTFE Surface Properties by Accelerated Aging Tests
- New Universal Tribometer as Pin or Ball-on-Disc and Reciprocating Pin-on-Plate Types
- Tribological Properties of Biodegradable Universal Tractor Transmission Oil
- ANN & ANFIS Models for Prediction of Abrasive Wear of 3105 Aluminium Alloy with Polyurethane Coating
Last modified: 2016-07-11 21:12:48