MICROSTRUCTURAL CHARACTERIZATION AND HOT EROSION BEHAVIOR OF CRC-NICR COATED STEEL USING HVOF TECHNIQUE

Erosion behavior of the High Velocity Oxygen Fuel (HVOF) deposited CrC - NiCr coating on stainless steel was evaluated. Th e solid particle erosion stu dy was conducted using an air jet erosion test rig at a velocity 60m/sec and impingement angle 60 ° , 75 ° and 90 ° , on HVOF spray coated steel at 600 ° C. Microstructure, chemical composition, phases present in the coating on the steel substrate was studied by using Scanning Electron Microscope (SEM) and X - Ray Diffraction method. The Hardness is gradually increasing with increasing content of Cr 3 C 2 particles in all three samples. The erosion mechanism of coatings was also discussed and erosion rate is maximum at impingement angle 75 ° .